O-1 OIL HARDENING DRILL ROD ROUND Carbon - .95% Manganese - 1.20% Silicon - .25% For ¼" round and larger, we carry oil hardening drill rod rather than water hardening. The O-1 in this size range is characterized by good machineability, smooth finish as well as superior dimensional stability and excellent hardening characteristics. We recommend it for use in dies, tools, parts, and punches. Excellent for general use in the shop. HARDENING: Heat slowly to 1475° F. - 1525° F. If a controlled furnace is not available, use 1500° Tempilaq. Hold at this temperature for a few seconds then quench in a light quenching oil. TEMPERING: Temper immediately. The following hardness table is for a one hour draw after oil quenching at 1500° F. Degrees F. Rockwell C Hardness As Hardened 63 - 65 300° 63 - 64 400° 61 - 62 500° 58 - 60 600° 54 - 56 700° 51 - 53 800° 46 - 48 900° 43 - 45
O-1 OIL HARDENING DRILL ROD ROUND Uhlík - .95% Mangan - 1.20% Křemík - .25% Pro kulaté tyče o průměru ¼" a větší nabízíme olejem kalené vrtací tyče namísto vodou kalených. O-1 v této velikostní kategorii se vyznačuje dobrou obráběcí schopností, hladkým povrchem, vynikající rozměrovou stabilitou a vynikajícími kalicími vlastnostmi. Doporučujeme jej pro použití v formách, nástrojích, dílech a raznicích. Vynikající pro běžné použití v dílně. KALENÍ: Pomalu zahřejte na 1475° F. - 1525° F. Pokud není k dispozici řízená pec, použijte 1500° Tempilaq. Držte při této teplotě několik sekund a poté ponořte do lehkého kalicího oleje. TEPLOTA: Okamžitě temperujte. Následující tabulka tvrdosti platí pro jedn hodinové vytvrzení po olejovém kalení při 1500° F. Stupně F. Rockwell C tvrdost Po zakalení 63 - 65 300° 63 - 64 400° 61 - 62 500° 58 - 60 600° 54 - 56 700° 51 - 53 800° 46 - 48 900° 43 - 45